CHEMCLAD SC is a two component, 100% solids, polymer system used for creating an outstanding corrosion and chemical resistant protective coating on all types of potable water equipment and structures.
CHEMCLAD SC is simple to use. It mixes easily and can be applied by brush or roller. It is
available in different colors to simplify overcoating. This high gloss coating yields a surface
that's not only functional, but also aesthetically pleasing.
CHEMCLAD SC provides extraordinary protection to machinery equipment and structures in some of the most severe industrial environments.
Prior to applying CHEMCLAD SC to concrete and / or cementitious substrates, the surface should be treated with CHEMCLAD® P4C to seal the surface, minimize outgassing and insure that optimum adhesion is obtained.
Click here for more information on NSF use.
- Outstanding Chemical Resistance
- Apply by Brush or Roller
- 100% Solids
- Unlimited Shelf Life
- Simple to Use
- Durable
Use on...
- Pipes
- Tanks
- Housings
- Pedestals
- Floors
- Containment Areas
Technical Data
- Volume capacity per kg.
- 48 in3 / 781 cc
- Mixed density
- 0.044 lbs per in3 / 1.28 gm per cc
- Coverage rate per kg. @ 6-7 mils
- 50 - 55 ft2 / 5 m2
- Shelf life
- Indefinite
- Volume Solids
- 100%
| Mixing ratio | Base | Activator |
|---|---|---|
| By Volume | 4.7 | 2 |
| By Weight | 3.29 | 1 |
Colors
Haze Gray
Gray
White
Note: Other colors are available on a “special order” basis. However, there are minimum / multiple quantity requirements for such orders and there may be an increase in cost. Additionally, due to formulation restrictions, not all colors are possible for all materials. Speak to your local ENECON Sales Representative for more information.
Due to monitor / printer differences, actual colors may vary slightly from the representations appearing in this chart.
Technical Data
- Volume capacity per kg.
- 48 in3 / 781 cc
- Mixed density
- 0.044 lbs per in3 / 1.28 gm per cc
- Coverage rate per kg. @ 6-7 mils
- 50 - 55 ft2 / 5 m2
- Shelf life
- Indefinite
- Volume Solids
- 100%
| Mixing ratio | Base | Activator |
|---|---|---|
| By Volume | 4.7 | 2 |
| By Weight | 3.29 | 1 |
Working Life and Cure Times
| Ambient Temperature | Working Life | Touch Dry | Maximum Overcoating | Full Cure | |
|---|---|---|---|---|---|
| 59°F | 15°C | 90 min. | 24 hrs. | 48 hrs. | 6 days |
| 77°F | 25°C | 70 min. | 16 hrs. | 24 hrs. | 4 days |
| 86°F | 30°C | 55 min. | 8 hrs. | 16 hrs. | 3 days |
Physical Properties
| Typical Values | Test Method | ||
|---|---|---|---|
| Tensile Shear Adhesion | |||
| Steel | 2300 psi | 162 kg/cm2 | ASTM D-1002 |
| Aluminum | 1700 psi | 120 kg/cm2 | ASTM D-1002 |
| Copper | 2200 psi | 156 kg/cm2 | ASTM D-1002 |
| Stainless Steel | 2500 psi | 176 kg/cm2 | ASTM D-1002 |
| Elcometer Adhesion - to properly prepared cementitious surfaces is greater than the cohesive strength of the substrate. | |||
Chemical Resistance
| Acetic acid (0-10%) | G | Methyl ethyl ketone | NR |
| Acetic acid (10-20%) | NR | Naptha | EX |
| Acetone | NR | Nitric acid (0-10%) | G |
| Aviation fuel (JP-4) | EX | Nitric acid (10-20%) | G |
| Butyl alcohol | EX | Phenol | NR |
| Calcium chloride | EX | Phosphoric acid (0-10%) | G |
| Carbon tetrachloride | G | Phosphoric acid (10-20%) | G |
| Chloroform | NR | Potassium chloride | EX |
| Crude oil | EX | Propyl alcohol | EX |
| Diesel oil | EX | Skydrol | G |
| Ethyl alcohol | G | Sodium chloride | EX |
| Gasoline | EX | Sodium hydroxide | EX |
| Heptane | EX | Sulfuric acid (0-20%) | EX |
| Hydrochloric acid (0-20%) | EX | Toluene | NR |
| Kerosene | EX | Trichlorethylene | NR |
| Methyl alcohol | G | Xylene | G |
EX - Suitable for most applications including immersion
G - Suitable for intermittent contact, splashes, etc.
NR - Not Recommended