Repair and protect all types of equipment subject to very aggressive abrasion.
Engineered to repair deeply damaged components.
METALCLAD CeramAlloy EBX is a three component, 100% solids, polymer composite specifically formulated to provide effective repair and rebuilding characteristics on all types of equipment subject to severe abrasion.
METALCLAD CeramAlloy EBX is a paste when mixed, so it is easily applied. When cured, however, CBX becomes a metal-hard, highly abrasion resistant compound engineered to repair deeply damaged components in the most aggressive abrasive environments.
METALCLAD CeramAlloy EBX is the best material to use to protect equipment subject to very aggressive abrasive environments.
Elbows, Pipes, Pumps, Chutes, Deflector Plates, Cyclones, Separators, Vibratory Feeders, Transfer Augers, etc.
- Extraordinary Abrasion Resistance
- Trowelable
- Requires No Heat
- Unlimited Shelf Life
- 100% Solids
- Safe & Simple To Use
Technical Data
- Volume capacity per 5 kg.
- 124 in3 / 2032 cc
- Mixed density
- 0.089 lbs per in3 / 2.46 gm per cc
- Coverage rate per 5 kg. @ 200 mils / 5mm
- 4.31 ft2 / 0.40 m2
- Shelf life
- Indefinite
- Volume Solids
- 100%
| Mixing ratio | Base | Activator | Aggregate |
|---|---|---|---|
| By Volume | 5 | 2 | 15 |
| By Weight | 7 | 2 | 20 |
Working Life and Cure Times
| Ambient Temperature | Working Life | Full Mechanical | Chemical Immersion | |
|---|---|---|---|---|
| 59°F | 15°C | 30 min. | 48 hrs. | 3 days |
| 77°F | 25°C | 20 min. | 24 hrs. | 2 days |
| 86°F | 30°C | 15 min. | 16 hrs. | 1 day |
Physical Properties
| Typical Values | Test Method | ||
|---|---|---|---|
| Compressive strength | 13,000 psi | 910 kg/cm2 | ASTM D-695 |
| Flexural strength | 5,000 psi | 350 kg/cm2 | ASTM D-790 |
| Hardness - Shore D | 86 | ASTM D-2240 | |
| Tensile Strength | 2,100 psi | 147 kg/cm2 | ASTM D-2370 |
| Tensile Shear Adhesion (CL+AC primer to substrate) | |||
| Steel | 4000 psi | 280 kg/cm2 | ASTM D-1002 |
| Aluminum | 2500 psi | 175 kg/cm2 | ASTM D-1002 |
| Copper | 3000 psi | 210 kg/cm2 | ASTM D-1002 |
| Stainless Steel | 4100 psi | 287 kg/cm2 | ASTM D-1002 |
Chemical Resistance
| Acetic acid (0-10%) | G | Methyl alcohol | G |
| Ammonium hydroxide (0-10%) | EX | Mineral Oil | EX |
| Aviation fuel | EX | Nitric acid (0-10%) | EX |
| Butyl alcohol | EX | Nitric acid (10-20%) | G |
| Calcium chloride | EX | Phosphoric acid (0-10%) | G |
| Crude oil | EX | Potassium chloride | EX |
| Diesel fuel | EX | Propyl alcohol | EX |
| Ethyl alcohol | G | Sodium chloride | EX |
| Gasoline | EX | Sodium hydroxide | EX |
| Heptane | EX | Sulfuric acid (0-10%) | EX |
| Hydrochloric acid (0-10%) | EX | Sulfuric acid (10-20%) | G |
| Hydrochloric acid (10-20%) | G | Toluene | G |
| Kerosene | EX | Xylene | EX |
EX - Suitable for most applications including immersion
G - Suitable for intermittent contact, splashes, etc.